环氧玻璃鳞片防腐粉末涂料常见型防腐涂料

  • 时间:
  • 浏览:856
  • 来源:正荣实业

环氧玻璃鳞片防腐粉末涂料是一种常见型防腐涂料,它属于一种双组份防腐涂料。组份一是由环氧树脂漆、玻璃鳞片、增韧剂、防沉剂等组成;组份二是固化剂。在使用是进行相关比较配比组合搅拌均匀后使用。当然还有一种为无溶剂环氧玻璃鳞片防腐涂料,它的溶剂为活性稀释剂均参与固化不含任何挥发性的气体,这种环氧玻璃鳞片防腐涂料的二组份为无溶剂固体剂

Epoxy glass flake anticorrosive powder coating is a kind of common type anticorrosive coating, it belongs to a kind of double component anticorrosive coating. Group a consists of epoxy resin paint, glass flake, toughening agent, anti settling agent and composition; component two is curing agent. The relationship between the ratio of combination in use is mixing after use. Of course, a non solvent epoxy glass flake anticorrosive paint, its solvent for gas active diluents were involved in curing does not contain any volatile, the epoxy glass flake anticorrosive paint two component solvent-free solid agent

猜你喜欢

低温固化型粉末涂料的制备研究

摘要:以三羟甲基丙烷(TMP)为主要原料,制备低温固化型粉末涂料。综合利用单因素分析和正交实验法研究了TMP的加入量、固化温度、以及固化时间对涂膜光泽度和冲击性能的影响,经过优

2021-09-24

技术分享|喷粉门板正流行?一文看懂静电粉末喷涂技术

早在2013年9月,国务院发布了《大气污染防治行动计划》对各行业提出了相关VOC限制标准。2018年1月1日,我国“史上最严”《中华人民共和国环境保护税法》正式推行,对用漆企业

2021-09-18

如何改善浅色粉末涂料的黄变问题

粉末涂料需要通过高温烘烤使粉末熔融,这个过程中浅色的粉末涂层容易发生黄变。造成粉末黄变的根本原因是发生过多的氧化反应,以下几种是常见导致过多氧化的因素:粉末在烤箱烘烤时间过长,

2021-09-17

燃气催化燃烧红外固化粉末涂料的固化参数研究

摘要:使用燃气催化燃烧红外固化聚酯+TGIC粉末涂料,分析固化时间以及固化温度对粉末涂层的影响;研究了不同固化参数下涂层的性能,由此确定催化红外固化粉末涂料的最优固化工艺。研究

2021-09-16

户外皱纹粉末涂料创新与应用

摘要:羟基聚酯/四甲氧甲基甘脲(TMMGU)型皱纹粉末涂料尽管不是新产品,但高价原材料限制其广泛应用,该体系粉末涂料的研究开发工作也很少。作者在大量的试验研究和实际应用经验基础

2021-09-11